Bushing made of PA (M14 - M16)
Bushing made of PA (M14 - M16)
 
   
No additional information available.
General Information For insulation of fasteners in the construction Prevent contact with... more

General Information

For insulation of fasteners in the construction

Prevent contact with conductive material and therefore short circuit

Prevent vibrations and loosening of parts

Resistant to electrolytic corrosion and thus indispensable

For connecting incompatible metals

Allow precise positioning and distance keeping of structural components

Chemical features:

Resistant to aromatic and aliphatic hydrocarbons, fuels, mineral oils and mineral lubricants; suitable for alkohols, esters, ketones, ethers and amines; good resistance to weak alkalis, but only moderate resistance to strong alkalis;

Limited resistance to weak mineral and organic acids; not resistant to oxidizing acids, strong mineral and organic acids as well as phenols; limited resistance to hydrolysis

Material specification:

Polyamide is an elastic, tough, loadable, but notch-sensitive material

Impact resistant

Resistant to abrasion and cold

High fatigue strength and excellent resilience

High wear resistance and good mechanical damping capacity

Insulating properties and an amazingly high tensile strength

Connecting parts made of polyamide and similar plastics protect from rust and corrosion damage

Polyamide can also be used in the food processing industry and in medical fields

PA 6 features a higher impact resistance compared to PA 6.6

PA 6 has the highest water absorption of all common plastics up to 9 to 10 % (followed by PA 6.6 with 8 to 9 %), thus considerably increased toughness, flexibility and elongation. However, the strength of the material can therefore be reduced by up to 10 %.

Material: PA 6 (polyamide 6)

Colour: natural

Density: approx. 1.14 g/cm3

Temperature range: -40 to +85 °C, for a short time +180 °C

Melting temperature: +220 °C (ISO 11357)

Yield stress: 75 MPa (ISO 527)

Elongation at break: >50 % (ISO 527)

Elastic modulus: 3,200 MPa (ISO 527)

Impact resistance: without break (DIN 53453)

Notch impact strength (Charpy): >3 kJ/m2 (ISO 179)

Ball pressure hardness: 160 N/mm2 (ISO 2039-1)

Shore hardness D: 82° (DIN 53505)

Dielectric strength: 20 kV/mm (IEC 60243)

Dielectric constant: 3.9 at 50 Hz (IEC 60250)

Surface resistance: 1013 Ohm (IEC 60093)

Volume resistivity: 1015 Ohm x cm (IEC 60093)

Comparative tracking index (CTI): >600 (DIN 53480)

Dielectric loss factor (at 50 Hz): 0.02 (specimen dry)

Water absorption: up to 10 % (during storage in water) (DIN 53472)

Flammability rating: UL 94 HB